C6782 (high power brass)
Alloy number | Characteristic | Use |
C6782
(high power brass) | C6782 is said to be high power brass and is the brass which added manganese and aluminum, iron. I am superior in strength as the name of the high power shows it and am good for forging characteristics and corrosion resistance between the heat. It is used as a propeller axis and the pump axis for the ship, the water pressure cylinder parts. | Forging, ship between the heat, parts for the mine |
Chemical ingredient
Alloy number | Cu | Pb | Al | Mn | Ni | Fe | Sn | As | Zn |
C6782
(high power brass) | 56.0 ...
60.5 | 0.50
The following | 0.20 ...
2.0 | 0.50 ...
2.5 | ― | 0.10 ...
1.0 | ― | -― | Residue |
(percent by weight)
※It can be manufactured by cadmium 75 ppm or less in C2700, C2800, C3602, C4641, C6782.
※Our JIS approval product is C3604 square and a rectangle.
Characteristic (reference level)
Alloy number | Quality | Tensile strength
N/mm² | Growth
% | Hardness
HV(5) | Cutting characteristics | The conductivity
IACS % | Machine workability | Bending characteristics | The extruded nature |
C6782
(high power brass) | Heat interval
Cold | 581
599 | 29
28 | 165
187 | 30 | 15.8 | 70 | X | 110 |
A note: ◎The X that is ○ suitable △ possibility suitable most is impossible
Manufacturing characteristics (I suppose it to be excellent cut brass = 100) The extruded nature (I suppose it to be excellent cut brass = 100)
Diameter of production range by the cross-section's greatest circumscribed circle
Alloy name | As pushing out | Drawing | ||
Straight angle | Variant | Straight angle | Variant | |
C6782 (high power brass) | 75 | 75 | 60 | 60 |
(unit mm)
Production range minimum section and wall thickness by the cross-section
Alloy name | As pushing out | Drawing | ||||||
Straight angle | Variant | Straight angle | Variant | |||||
Area
㎜² | Thickness
㎜ | Area
㎜² | Thickness
㎜ | Area
㎜²
| Thickness
㎜
| Area
㎜²
| Thickness
㎜
| |
C6782 (high power brass) | 24 | 3 | 24 | 3 | 27 | 3 | 27 | 3 |
(unit mm)